Castable Refractory Cement : Whyt Heat A , K, C

We guarantee our valued clients with superior quality Castable Refractory Cement. The offered cement is well-known for there compressive strength and longer shelf life. Supreme grade raw-materials and compounds are obtained from the authorized vendors of the market to manufacture the cement. We process the cement in our huge infrastructure facility by making use of modern production techniques. Moreover, we offer the Castable Refractory Cement in special packages to prevent moisture from damaging the cement.

Castables: WhytHeat A, K and C

WhytHeat castables are produced in three grades, designated as WhytHeat-A, WhytHeat-K andWhytHeat-C. All contain the special high purity, high alumina refractory binder CAL-AL-75. Typical properties of these castables, including data on strength, conductivity and chemical composition are provided in the table at the bottom of this page. Each grade of WhytHeat castables is used for a specific service temperature and environment.

WhytHeat-A
WhytHeat-A is a high purity, high alumina castable of exceptional quality with an alumina content of over 90% and with very low silica and iron contents. Hence, it is used for service temperatures up to 1750ºC and can resist attack from process gas atmospheres containing carbon monoxide and hydrogen. WhytHeat-A is particularly suitable for use in coke ovens, gas production plants as well as gasification plants and is also used in the iron and steel industry for lining blast furnaces and for skew backs, ports and roof lining of arc-melting furnaces , in the non-ferrous metal industry to line reverberatory furnaces where high purity aluminium is produced in reactors of refineries as well as in fertiliser plants where castables with a high degree of resistance to carbon monoxide, hydrogen and ammonia are desired for lining of  reheaters/converters and on all transfer lines

WhytHeat-K
WhytHeat-K, which has an alumina content of 60% can be used for service temperatures upto 1600ºC. This castable also has a low iron content and can resist carbon monoxide attack.

WhytHeat-C
WhytHeat-C is a castable with about 50% alumina and serves as a general purpose high temperature castable required for service temperatures up to 1500ºC. 

Packaging and Storage
WhytHeat castables are available in HDPE packages of 50kg. The shelf life of White Heat castables is six to nine months under ideal storage conditions.


Product Data:

Mortars: ACCOSET 50

MORTARS
Product: ACCOSET 50 (N)*
Type: 50% Alumina Mortar (Coarse)
Nature of Bond: Chemical/Ceramic
General Properties
Raw Material Base: Calcined Bauxite
Max. Service Temperature: 1550 ºC
Sintering Temperature: 1100 ºC
Max. Grain Size 1.5 mm
Chemical Analysis
Typical Value Specification
Al2O3 % 51.90 50 min.
SiO2 % 32.6 -
Fe2O3 % 3.60 4.0 max.
TiO2 % 5.80 -
CaO 0.80 -
LOI % 5.00 -
Physical Properties
Typical Value Specification
Water for trowelling consistency % 24 ~ 28 -
Water required for ramming consistency % 10 ~ 20 -
Transverse strength
after drying at 110 ºC for 24 hours (kg/cm2)
17.0 -
% Retained above maximum size 2 5.0 max.
Thermal Properties
Typical Value Specification
Pyrometric cone equivalent (orton/ºC) 32/1717 31.5/1699

Refractory Mortar :ACCOSET 50